TA15 粉末激光成形基板应力影响因素的试验研究
Alternative TitleExperimental Research on Influencing Factors of the Residual Stress of Substrate in Ti-6.5Al-1Mo-1V-2Zr Powder Laser Shaping
来佑彬; 刘伟军; 赵宇辉; 王福雨
Source Publication稀有金属材料与工程
Indexed BySCI ; EI ; CSCD
EI Accession number20143600063408
WOS IDWOS:000339783500014
Contribution Rank1
KeywordTa15 粉末激光成形 压痕法 基板 残余应力
Abstract为了研究TA15(Ti-6.5Al-1Mo-1V-2Zr)粉末激光成形基板残余应力的影响因素,成形出19 个不同工艺参数的试件,采用压痕法分别对其进行残余应力的测量,总结出激光功率、送粉速度、激光扫描速度、成形层数、扫描转角等参数对基板残余应力的影响。研究表明,随着激光功率的增大,基板残余应力数值随之增大,当功率高于1700 W 时,基板残余应力开始减小;基板残余应力在送粉速度为0.5~1 g/min 和1.5~2 g/min 2 个区间内,表现出随着送粉速度的增大残余应力减小的情况,而在1~1.5 g/min 区间内表现出相反的情况;基板残余应力随着扫描速度的增大呈现出先增大后减小的趋势;基板残余应力随成形层数的增加而递减;对于不同扫描转角的测试件,扫描转角为60°的情况下,基板残余应力值最小,而30°扫描转角情况下,基板残余应力值最大。
Other AbstractIn order to study the influencing factors of residual stress of the Ti-6.5Al-1Mo-1V-2Zr powder laser shaping substrate, 19 samples were formed with different process parameters, and then an indentation method was used to measure their residual stress. The effects of the laser power, the powder feeding rate, the laser scanning speed, the number of shaping layers and the angle of laser scanning on the substrate residual stress were summarized. The results show that the substrate residual stress is increased with the increase of the laser power. However, the stress begins to decrease when the laser power is larger than 1700 W. When the powder feeding rate range is from 0.5 to 1 g/min or from 1.5 to 2 g/min, the residual stress decreases with the increase of the powder feeding rate. But when the powder feeding rate is between 1 similar to 1.5 g/min the residual stress increases with higher powder feeding rate. In addition, with the increase of the scanning speed the substrate residual stress increases and then decreases. The residual stress of the substrate decreases with the number of layers increasing. To the samples with different scanning angles, the residual stress of the substrate is smaller at 60 scanning angle than at other scanning angles, while the maximum value of the substrate residual stress occurs at 30 degrees.
WOS HeadingsScience & Technology ; Technology
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
Citation statistics
Cited Times:4[CSCD]   [CSCD Record]
Document Type期刊论文
Corresponding Author来佑彬
Affiliation1.Modern Equipment Research Laboratory, Shenyang Institute of Automation, Chinese Academy of Sciences, Shenyang , China
2.University of Chinese Academy of Sciences, Beijing , China
Recommended Citation
GB/T 7714
来佑彬,刘伟军,赵宇辉,等. TA15 粉末激光成形基板应力影响因素的试验研究[J]. 稀有金属材料与工程,2014,43(7):1605-1609.
APA 来佑彬,刘伟军,赵宇辉,&王福雨.(2014).TA15 粉末激光成形基板应力影响因素的试验研究.稀有金属材料与工程,43(7),1605-1609.
MLA 来佑彬,et al."TA15 粉末激光成形基板应力影响因素的试验研究".稀有金属材料与工程 43.7(2014):1605-1609.
Files in This Item:
File Name/Size DocType Version Access License
TA15粉末激光成形基板应力影响因素的试(308KB)期刊论文出版稿开放获取ODC PDDLView Application Full Text
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[来佑彬]'s Articles
[刘伟军]'s Articles
[赵宇辉]'s Articles
Baidu academic
Similar articles in Baidu academic
[来佑彬]'s Articles
[刘伟军]'s Articles
[赵宇辉]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[来佑彬]'s Articles
[刘伟军]'s Articles
[赵宇辉]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: TA15粉末激光成形基板应力影响因素的试验研究.pdf
Format: Adobe PDF
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.